Q1: What is the grade or specification of the pure nickel used in this product?
A1: The pure nickel used in this product is typically 99.9% pure nickel (also known as Nickel 200 or Nickel 201) which complies with standard material specifications like ASTM B162 or UNS N02200.
Q2: What is the thickness of the nickel sheet plate?
A2: The thickness of the nickel sheet plate can vary depending on the customer's requirements, but common thickness ranges are from 0.5mm to 10mm. You would need to confirm the specific thickness required for your application.
Q3: What are the main applications of pure nickel plates?
A3: Pure nickel plates are widely used in applications where high corrosion resistance and high-temperature stability are required, such as in chemical processing, electronics, aerospace, battery production, and marine environments.
Q4: Is the 30-meter length of the nickel sheet plate a single piece or multiple pieces?
A4: The 30-meter length could either be supplied as a single continuous sheet or divided into multiple sheets depending on the manufacturer or the specific order requirements. It's essential to confirm with the supplier.
Q5: Does the nickel sheet plate come with any surface treatment or coating?
A5: Pure nickel plates are often supplied with a smooth surface finish, but additional treatments like polishing, brushing, or coating (e.g., passivation or electroplating) can be done based on the application and customer needs. It's important to specify any additional treatments when placing an order.
| Grade | N4 | N6 | Nickel 201 | Nickel 200 | |
| Chemical Composition(%) | Ni | -- | -- | ≥99 | ≥99.2 |
| Ni+Co | 99.9 | 99.5 | -- | -- | |
| Cu | ≤0.015 | 0.1 | ≤0.25 | ≤0.25 | |
| Si | ≤0.03 | 0.1 | ≤0.35 | ≤0.35 | |
| Mn | ≤0.002 | 0.05 | ≤0.35 | ≤0.35 | |
| C | ≤0.01 | 0.1 | ≤0.02 | ≤0.15 | |
| Mg | ≤0.01 | 0.1 | -- | -- | |
| S | ≤0.001 | 0.005 | ≤0.01 | ≤0.01 | |
| P | ≤0.001 | 0.002 | -- | -- | |
| Fe | ≤0.04 | 0.1 | ≤0.4 | ≤0.4 | |
| Physical Properties | |
| Density | 8.89g/cm3 |
| Specific Heat | 0.109(456 J/kg.ºC) |
| Electrical Resistivity | 0.096 x 10-6ohm.m |
| Melting Point | 1435-1450ºC |
| Thermal Conductivity | 70.2 W/m-K |
| Mean Coeff Thermal Expansion | 13.3x10-6m/m.ºC |
| Mechanical Properties | |
| Mechanical Properties | Nickel 200 |
| Tensile Strength | 462 Mpa |
| Yield Strength | 148 Mpa |
| Elongation | 47% |