Nickel201 material chemical composition and physical properties
Nickel201 pure nickel alloy
Nickel Alloy 201
Nickel 201, LC Nickel 99.2; Alloy 201
Commercially pure (99.6%) wrought nickel is essentially the same as Nickel 200 but has a lower carbon content to prevent intergranular carbon embrittlement at temperatures above 600°F (315°C). The lower carbon content also reduces hardness, making Nickel 201 particularly suitable for cold formed products.
Available product forms:
Pipes, tubes, plates, strips, plates, round bars, flat bars, forged billets, hexagonal and wire rods.
product specifications
Nickel 201 is designated UNS N02201 and Werkstoff numbers 2.4061 and 2.4068.
Nickel 200 specifications include:
Rods and Rods: ASTM B 160; ASME SB 160, DIN 17752, ISO 9723, VdTÜV345.
Pipe and tube: ASTM B 161; ASME SB161, ASTM B 163; ASME SB 163, ASTM B 725; ASMESB 725, ASTM B730; ASME SB 730, ASTM B 751; ASME SB 751, ASTM B775; ASME SB 775, ASTM B 829; ASME SB 829, DIN 17751, ISO 6207, BS3074 (NA12), VdTÜV345.
Sheet, plate and strip: ASTM B 162/ASME SB 162, DIN 17750, ISO 6208, BS3072-3073 (NA12), SAE AMS 5553, VdTÜV345.
Accessories: ASTM B 366 / ASME SB 366
Forgings: ISO 9725, DIN 17754
Chemical composition: DIN 17740
Wire: DIN 17753, ISO 9724
chemical composition
Limit chemical composition, weight %
Nickel (plus cobalt) 99.0
Copper 0.25
Iron 0.40
Manganese 0.35
Carbon 0.15
Silicon 0.35
Sulfur 0.01